TCS-30 – 25.75kg Processing
Before measuring out the components, pre-mix Part A and Part B separately (this mixes any components that may separate during storage).
- Measure out required amounts of Part A and B into mixing container and mix thoroughly for 3 minutes making sure to scrape the sides and bottom of the mixing container several times.
- Transfer mixed material into clean mixing container and stir again.
Be careful not to whip and beat the material during the mixing process as this introduces unnecessary air bubbles.
For best results after mixing, vacuum de-air material before casting (29 inches of mercury required) and allow for up to 5 x expansion during the vacuum process. For faster demold time, catalyst can be increased up to 4% (please note that this will decrease pot life). Above mentioned percentages are by weight.
Brush-On applications
For brush-On applications and for the silicone to hold a vertical surface, silicone thixo should be added to increase viscosity. By weight 0.5% (thick), 1% (thicker), 2% maximum dosage (thickest).
For a Block & cavity molds
For a Block & Cavity molds (where the silicone is poured) silicone thinning fluid can be added to reduce viscosity which assists in reducing air bubbles and capturing intricate surface detail. Max dosage by weight 10%. Please note that by adding silicone thinner, Shore A hardness and tear strength are proportionally reduced.
TCS-30 – 25.75kg Pouring
for best results, pour the silicone rubber in a thin stream to the lowest part of the mold in a single spot and allow material to flow around the model and self-level. It is suggested to cover the model by at least 10 mm.
TCS-30 – 25.75kg Curing/Post curing
Allow the mold to cure for 24 hours at room temperature (23°C) before demolding. Post curing the mold an additional 4-6 hours at 80 °C will eliminate any residual moisture and alcohol that is a by-product of the condensation reaction that can inhibit the cure of some urethane resins and rubbers. Allow mold to cool to room temperature before using. Do not cure rubber where temperature is less than 23°C. The silicone molds can be cleaned with mild soap and water then rinsed and left to dry.
TCS-30 – 25.75kg Mold performance & storage
The physical life of the mold depends on how you use it (materials cast, frequency etc.). Casting abrasive materials such as concrete can quickly deteriorate mold detail, while casting non-abrasive materials like wax or plaster will not affect mold detail. Before storing, the mold should be cleaned with soap & water solution and wiped fully dry. Two-part (or more) molds should be assembled. Moulds should be stored on a level surface in a cool, dry environment. Casting Plaster into the mold prior storing will extent mold library life.